Rust-Oleum CombiColor Original Satin Finish

RUST-OLEUM® CombiColor Metal 7300/7400 coating- is a primer and topcoat in one, based on a urethane modified alkyd, providing good drying properties at low temperatures. The product contains rust-inhibitive pigments and is lead- and chromate free.

RECOMMENDED USE -RUST-OLEUM CombiColor Original 7300/7400 should be applied on bare, manually derusted or with CombiPrimer Anti-Corrosion 3369/3380 primed steel. CombiColor Original is intended for brush and roller application and can also be applied by air spray. RUSTOLEUM CombiColor Original 7300/7400 offers corrosion protection in a light industrial environment. For metal structures in a more aggressive industrial environment, priorapplication of a RUST-OLEUM CombiPrimer Anti-Corrosion 3369/3380 is recommended.

DRY TIMES

Touch dry: 2 hours (20°C), 3 hours (10°C), 1 ½ hours (30°C)

Dry to handle: 8 hours (20°C), 16 hours (10°C), 6 hours (30°C)

Dry to recoat: 16 hours (20°C), 24 hours (10°C), 8 hours (30°C)

Fully cured: 7 days (20°C), 14 days (10°C), 5 days (30°C)

CVOVERAGE- 10.3 m²/litre

SURFACE PREPARATION- Remove oil, grease and all other surface contaminations by alkaline or high pressure (steam) cleaning in combination with appropriate detergents. Remove rust scale, loose mill scale,loose rust and loose coatings by scraping and wire brushing to St 3 (ISO 8501-1 : 1988), light blast cleaning or sanding. Sand intact coatings to roughen the surface slightly. The surface must be clean and dry during application. Galvanised, Zinc and Aluminium surfaces have to be primed first with CombiPrimer Tack Coat 3302.

DIRECTIONS FOR USE- please thoroughly stirred prior to use.

APPLICATION CONDITIONS- Temperature of air, substrate and coating material between 5° and 35°C

APPLICATION & THINNING-

BRUSH- up to 10% volume

ROLLER- up to 10% volume (Roller Application may require 2 coats to achieve recommended dry film thickness)

AIR-ATOMISED SPRAY-10-25% volume RUST-OLEUM Thinner 7301. Gravity cup and pressure cup. Tip size: 1.0 -1.5 mm. Atomising pressure: 2 - 4 bar.

Popular colours include black and white.